956010 2K epoxy adhesive

Design and use:

DP110:

- short processing time (8-10 minutes)

- first load on the joined parts possible after a short time

- tough elastic

- high shear strength (18 MPa)

- good peel strength (35 N/cm), impact resistance and aging properties

- made of epoxy resin

- low flow behavior

- hand-tight after approx. 20 minutes

- operating temperature -55 °C to +80 °C

- for bonding metals, plastics such as ABS, GRP, PC etc. and other materials

- suitable mixing nozzle: 9560150021

DP490:

- very long processing time (more than 90 minutes)

- thixotropic: does not flow on vertical surfaces

- tough elastic

- high shear strength (30 MPa)

- good peel strength (92 N/cm) and impact resistance

- based on epoxy resin

- hand-tight after approx. 4 hours

- operating temperature from -55 °C to +120 °C

- temperature resistance 120 °C

- for bonding metals such as aluminum, steel or brass, plastics such as ABS, PA, PC, hard PVC etc. as well as fiber composites

- suitable mixing nozzle: 9560150021

DP8005:

- very short processing time (2-3 minutes)

- rapid strength build-up

- bonding of low-energy plastics without pre-treatment of the surfaces

- first load on the joined parts possible after a very short time

- tough-elastic

- high shear strength (6 MPa)

- good peel strength (28 N/cm) and impact resistance

- made of acrylate

- low flow behavior

- hand-tight after approx. 30 minutes

- operating temperature from -55 °C to +80 °C

- for bonding PE, PP and TPE as well as ABS, hard PVC, PMMA, fiber composites, painted and primed metals, glass, wood, etc.

- suitable mixing nozzle: 9560150022